A weld-on magnesium hull anode for freshwater cathodic protection.

MG Duff Logo

Add to your basket...

MG Duff MD78 Magnesium (Fresh Water) Weld On Bar Anode - 305mm (SG056BA)

By: MG Duff, Part No.: MD78

Availability: This item is currently out of stock, we will send your order as soon as it is available

Price:
£45.50
SRP:
£62.23
You save:
£16.73 (27%)
Quantity:

MG Duff MD78 Magnesium (Fresh Water) Weld On Bar Anode Information

Our thoughts...

It is important to remember NOT to paint anodes when antifouling. Doing so will prevent the anode from working and may cause expensive problems.

This MG Duff magnesium weld-on hull anode for use in freshwater conditions is designed to help guard against corrosion of underwater gear such as propellers, shafts, and rudders which are vital to the vessel and are expensive items to replace; the failure of a propeller or rudder could have disastrous consequences.

The weld-on anode is directly welded to the hull of the boat.

If corrosion is allowed to persist the effects can vary from the pitting of propellers and shafts to the decomposition of the alloy. The failure of something as small and inexpensive as a split pin can result in the loss of the propeller.

Underwater corrosion control is an essential maintenance task and something to consider. It is relatively easy to replace existing anodes and install new cathodic protection systems if required.

What is cathodic protection?

Cathodic protection is an electrochemical process that halts the natural reaction (corrosion) of metals in a particular environment by superimposing an electrochemical cell more powerful than the corrosion cell.

Sacrificial Anodes are fitted or bonded to the metal to be protected which in turn as it has a greater electrical potential than the anode material becomes cathodic and causes the anode to waste instead of itself. In a correctly installed cathodic protection system, the only corrosion occurs to the sacrificial anode which is replaceable.

The number and size of anodes are determined by the type of material and the surface area being protected.

Which anode should I choose?

As a general rule owners should fit the anodes suitable for the environment they most regularly berth in and the following list provides a useful guide:

  • Freshwater - Fit Magnesium anodes
  • Brackish water - Fit Aluminium anodes (Brackish water is a mixture of fresh water and saltwater, commonly associated with estuary waters).
  • Saltwater - Fit Zinc or Aluminium anodes

Not all anodes are suitable for every environment, for example, the surface of zinc or aluminium anodes will if left in freshwater for some time become covered with an off-white crust of oxide which effectively seals the anode and stops it from working even when returned to saltwater.

Zinc anodes suffer a similar problem even in brackish conditions whereas aluminium will continue to operate effectively in river estuaries and other areas of brackish water indefinitely. The consequences of this passivation of the anode are that the next most anodic item within the anode bonding system will start to sacrifice itself which could of course be very serious.

Owners must be aware of the effects that this may have on their boats and fit the correct cathodic protection system to avoid corrosion.

MG Duff MD78 Magnesium (Fresh Water) Weld On Bar Anode Specification

Width 79mm
Depth 32mm
Length 385mm
Anode Length 305mm
Weight 1.5Kg

Please note: Magnesium anodes are not suitable for wooden hull vessels as they can damage the timber. Please contact us for further information.

You may also like...

Hempel Underwater Primer - 750ml
from £22.95
Save: £4.09 (15%)
Hempel Classic Antifouling 2.5L
from £47.99
Save: £8.17 (15%)
Hempel Cruising Performer Antifoul 2.5L
from £74.95
Save: £23.77 (24%)

Explore similar items...